Nonferrous Metal Products – Delivery Program
Brass Powder (Copper-Zinc)
DIN
EN 12 163 to 12 168/12 420/12 449/12 451/1652/1653
Range of
alloys |
|
approx.
Density |
Chemical
Composition % |
Comparable
Specifications* |
Cu Zn39 Pb3
|
CW614N
|
2,5 ÷ 4.5 |
Cu 57,0 -59,0
Pb 2,5 -3,5
Zn bal. |
Cu Zn39 Pb3, DIN 17 660
C 38 500 UNS
CZ 121- Pb3 BS 2870 - 2875
Cu Zn39 Pb3, ISO 426 |
Cu Zn 38 Pb 1
|
CW607N
|
2,5 ÷ 4.5
|
Cu 60,0- 61,0
Pb 0,8 -1,6
Zn bal. |
Cu Zn38 Pb1,5, DIN 17 660
C 35 300, C 37 000 UNS
CZ 128 BS 2870 - 2875
Cu Zn37 Pb1, Cu Zn37 Pb2, ISO 426 |
Cu Zn 35 Pb 1
|
CW600N
|
2,5 ÷ 4.5
|
Cu 62,5- 64,0
Pb 0,8 -1,6
Zn bal. |
Cu Zn36 Pb1,5, DIN 17 660
C 34 500, C 34 700 UNS
CZ 118, CZ 119 BS 2870 - 2875
Cu Zn35 Pb1, Cu Zn34 Pb2, ISO 426 |
Cu Zn 36 Pb2 As
|
CW602N |
2,5 ÷ 4.5 |
Cu 61,0-63,0
Pb 1,7-2,8
As 0,02-0,15
Zn bal.
|
C 35 330 UNS |
Cu Zn37
|
CW508L
|
2,5 ÷ 4.5
|
Cu 62,0-64,0
Zn bal.
|
Cu Zn37, DIN 17 660
C 27 200, C 27 400 UNS
CZ 108 BS 2870 - 2875
Cu Zn37, ISO 426 |
Cu Zn40
|
CW509L
|
2,5 ÷ 4.5
|
Cu 59,5-61,5
Zn bal.
|
Cu Zn40, DIN 17 660
C 28 000 UNS
CZ 109 BS 2870 - 2875
Cu Zn40, ISO 426 |
|
Range of
alloys |
|
approx.
Density |
Chemical
Composition % |
Comparable Specifications* |
|
Cu Zn37 Mn3 Al2 Pb Si
|
CW713R
|
2,5 ÷ 4.5
|
Cu 57,0-59,0
Mn 1,5-3,0
Al 1,3 - 2,3
Pb 0,2 - 0,8
Si 0,3 -1,3
Zn bal. |
Cu Zn40 Al2, DIN 17 660
C 67 400 UNS
CZ 135 BS 2870 -2875
Cu Zn37 Mn3 Al2 Si, ISO 426 |
|
Cu Zn39 Mn1 Al Pb Si |
CW718R
|
2,5 ÷ 4.5
|
Cu 57,0-59,0
Mn 0,8-1,8
Al 0,3 -1,3
Pb 0,2 - 0,8
Si 0,2 - 0,8
Zn bal. |
Cu Zn40 Al1, DIN 17 660
CZ 114 BS 2870-2875 (~ 1% Pb) |
|
Cu Zn35 Ni3 Mn2 Al Pb |
CW710R
|
2,5 ÷ 4.5
|
Cu 58,0- 60,0
Ni 2,0 - 3,0
Mn 1,5- 2,5
Al 0,3 -1,3
Pb 0,2 - 0,8
Zn bal. |
Cu Zn35 Ni2, DIN 17 660 |
|
Cu Zn40 Mn2 Fe1 |
CW723R
|
2,5 ÷ 4.5 |
Cu 56,5-58,5
Mn 1,0- 2,0
Fe 0,5 -1,5
Zn bal. |
Cu Zn40 Mn2, DIN 17 660 |
|
Cu Zn38 Sn1 As |
CW717R
|
2,5 ÷ 4.5
|
Cu 59,0-62,0
Sn 0,5-1,0
As 0,02-0,06
Zn bal.
|
Cu Zn38 Sn1, DIN 17 660
C 46 400 UNS
CZ 112 BS 2870 - 2875
Cu Zn38 Sn1, ISO 426 |
|
Cu Zn28 Sn1 As |
CW706R
|
2,5 ÷ 4.5
|
Cu 70,0 - 72,5
Sn 0,9 -1,3
As 0,02 -0,06
Zn bal. |
Cu Zn28 Sn1, DIN 17 660
C 44 300 UNS
CZ 111 BS 2870 - 2875
Cu Zn28 Sn1, ISO 426 |
|
Cu Zn23 Al6 Mn4 Fe3 Pb |
CW704R |
2,5 ÷ 4.5 |
Cu 63,0- 65,0
Al 5,0 - 6,0
Mn 3,5 -5,0
Fe 2,0 -3,5
Pb 0,2 - 0,8
Zn bal. |
Cu Zn23 Al6 Mn4 Fe3, DIN 17 660
C 67 000 UNS
CZ 116 BS 2870 - 2875 |
|
Cu Zn31 Si1 |
CW708R |
2,5 ÷ 4.5
|
Cu 66,0-70,0
Si 0,7-1,3
Zn bal. |
Cu Zn31 Si1, DIN 17 660 |
|
Cu Zn20 Al2 As |
CW702R |
2,5 ÷ 4.5 |
Cu 76,0 -79,0
Al 1,8 - 2,3
As 0,02 -0,06
Zn bal. |
Cu Zn20 Al2, DIN 17 660
C 68 700 UNS
CZ 110 BS 2870 - 2875
Cu Zn20 Al2, ISO 426 |
Range of alloys |
|
approx.
Density |
Chemical
Composition % |
Mechanical
Properties |
Comparable
Specifications* |
Cu Zn35
Mn2 Al 1 Fe1-C |
CC765S |
2,5 ÷ 4.5
|
Cu 57,0 -65,0
Mn 0,5-3,0
Al 0,5 - 2,5
Fe 0,5 -2,0
Zn bal. |
GZ/GC:
Rm ≥ 500
Rp 0,2 ≥ 200
A5 ≥ 18
HB ≥ 120 |
Cu Zn35 Al1, DIN 1709
C 86 400 UNS
HTB 1 BS 1400
Cu Zn35 Al Fe Mn, ISO 1338 |
Cu Zn34
Mn3 Al2 Fe1-C |
CC764S
|
2,5 ÷ 4.5
|
Cu 55,0 -66,0
Mn 1,0 - 4,0
Al 1,0 -3,0
Fe 0,5 -2,5
Zn bal. |
GZ:
Rm ≥ 620
Rp 0,2 ≥ 260
A5 ≥ 14
HB ≥ 150 |
Cu Zn34 Al2, DIN 1709
C 86 200 UNS
HTB 2 BS 1400 |
Cu Zn25 Al5
Mn4 Fe3-C |
CC762S |
2,5 ÷ 4.5
|
Cu 60,0 -67,0
Mn 2,5-5,0
Al 3,0 -7,0
Fe 1,5- 4,0
Zn bal. |
GZ/GC:
Rm ≥ 750
Rp 0,2 ≥ 480
A5 ≥ 5
HB ≥ 190 |
Cu Zn25 Al5, DIN 1709
C 86 300 UNS
HTB 3 BS 1400
Cu Zn25 Al Fe3 Mn3, ISO 1338 |
|
Cu Zn16 Si4-C |
CC761S |
2,5 ÷ 4.5
|
Cu 78,0-83,0
Si 3,8-5,0
Zn bal.
|
GZ/GM:
Rm ≥ 500
Rp 0,2 ≥ 300
A5 ≥ 8
HB ≥ 130 |
Cu Zn15 Si 4, DIN 1709
C 87 400, C 87 500, C 87 800 UNS |
Cu Zn 37 Al1-C
|
CC766S |
2,5 ÷ 4.5
|
Cu 60,0-64,0
Al 0,3-1,8
Zn bal.
|
GM:
Rm ≥ 450
Rp 0,2 ≥ 170
A5 ≥ 25
HB ≥ 105 |
Cu Zn37 Al1, DIN 1709 |
|
|